High Strength & High Corrosion Resistant Structural Thermoset Composites
Please note: all of our materials are custom developed to meet your specific requirements, if you don't see a product performance metric that meets your needs, call us to discuss your specific project requirements at 317.773.1766 or email us at sales-usa@idicomposites.com.
High Strength & High Corrosion Resistant Structural Thermoset Composites
STC® 2200 Series – High Strength Polyester/Vinyl Ester Hybrid Composites |
|||||||
Properties |
STC®-2252 |
STC®-2253FR |
|||||
Imperial |
SI |
Imperial |
SI |
||||
Impact Strength-Izod Notched |
25 ft.lb./in. |
1,330 J/m |
30 ft.lb./in. |
1,600 J/m |
|||
Flexural Strength |
38,000 psi |
262 MPa |
45,000 psi |
310 MPa |
|||
Flexural Modulus |
2,000 ksi |
14 GPa |
2,000 ksi |
14 GPa |
|||
Tensile Strength |
27,000 psi |
186 MPa |
30,000 psi |
207 MPa |
|||
Tensile Modulus |
2,800 ksi |
19 GPa |
2,500 ksi |
17 GPa |
|||
Water Absorption (24 Hrs @ 23C) |
0.1 to 0.3% |
0.1 to 0.3% |
|||||
Specific Gravity |
1.6 to 1.8 |
1.6 to 1.8 |
|||||
Shrinkage |
0.0 to 0.2% |
0.1 to 0.3% |
|||||
Barcol Hardness |
30 to 60 |
30 to 60 |
|||||
Click to download a pdf of the STC® 2200 Series Data Sheet |
|||||||
The information on this sheet is a guide. The stated values reflect an average of several tests conducted on CI's goods. These values were obtained under ideal conditions and may not be replicated in any particular test, part, or application. Because the values achieved in actual parts depend considerably on part design, molding conditions, and testing methods, no guarantee is made or implied regarding values to be obtained in any specific test, part, or application. CI makes no warranty or representation as to the suitability of any of its goods for use in any application. CI relies on customer to conduct its own tests and judge for itself the suitability of CI's goods.