High Strength Structural Thermoset Composites
Please note: all of our materials are custom developed to meet your specific requirements, if you don't see a product performance metric that meets your needs, call us to discuss your specific project requirements at 317.773.1766 or email us at sales-usa@idicomposites.com.
High Strength Structural Thermoset Composites
STC® 1000 Series – Polyester, Vinyl Ester and Hybrid Composites |
|||||||
Properties |
STC®-1023 |
STC®-1146A |
STC®-1246 |
||||
Imperial |
SI |
Imperial |
SI |
Imperial |
SI |
||
Impact Strength-Izod Notched |
14 ft.lb./in. |
747 J/m |
32 ft.lb./in. |
1,710 J/m |
24 ft.lb./in. |
1,280 J/m |
|
Flexural Strength |
20,000 psi |
138 MPa |
37,000 psi |
255 MPa |
32,000 psi |
221 MPa |
|
Flexural Modulus |
1,800 ksi |
12 GPa |
2,300 ksi |
16 GPa |
2,300 ksi |
16 GPa |
|
Tensile Strength |
10,000 psi |
69 MPa |
15,000 psi |
103 MPa |
13,000 psi |
90 MPa |
|
Tensile Modulus |
-- |
2,700 ksi |
19 GPa |
2,600 ksi |
18 GPa |
||
Water Absorption (24 Hrs @ 23C) |
0.1 to 0.3% |
0.1 to 0.3% |
0.1 to 0.3% |
||||
Specific Gravity |
1.7 to 1.9 |
1.55 to 1.75 |
1.6 to 1.8 |
||||
Shrinkage |
0.1 to 0.3% |
0.1 to 0.3% |
0.1 to 0.3% |
||||
Barcol Hardness |
30 to 50 |
30 to 50 |
30 to 50 |
||||
Bulk Factor App. |
1 |
1 |
1 |
||||
Dielectric Strength |
400 KV/in. |
16 KV/mm |
-- |
-- |
|||
Arc Resistance |
180+ Seconds |
-- |
-- |
||||
Heat Deflection Temp @ 264 psi |
>500 F |
>260 C |
-- |
-- |
|||
Flame Resistance @ 1/16" |
V-0 Compliant |
-- |
-- |
||||
Click to download a pdf of the STC® 1000 Series Data Sheet |
|||||||
The information on this sheet is a guide. The stated values reflect an average of several tests conducted on CI's goods. These values were obtained under ideal conditions and may not be replicated in any particular test, part, or application. Because the values achieved in actual parts depend considerably on part design, molding conditions, and testing methods, no guarantee is made or implied regarding values to be obtained in any specific test, part, or application. CI makes no warranty or representation as to the suitability of any of its goods for use in any application. CI relies on customer to conduct its own tests and judge for itself the suitability of CI's goods.